Polyester

From Infogalactic: the planetary knowledge core
Jump to: navigation, search

<templatestyles src="Module:Hatnote/styles.css"></templatestyles>

SEM picture of a bend in a high-surface area polyester fiber with a seven-lobed cross section
Close-up of a polyester shirt
Stretching polyester fabric

Polyester is a category of polymers that contain the ester functional group in their main chain. As a specific material, it most commonly refers to a type called polyethylene terephthalate (PET). Polyesters include naturally occurring chemicals, such as in the cutin of plant cuticles, as well as synthetics through step-growth polymerization such as polybutyrate. Natural polyesters and a few synthetic ones are biodegradable, but most synthetic polyesters are not. This material is used very widely in clothing.

Depending on the chemical structure, polyester can be a thermoplastic or thermoset. There are also polyester resins cured by hardeners; however, the most common polyesters are thermoplastics.[1]

Fabrics woven or knitted from polyester thread or yarn are used extensively in apparel and home furnishings, from shirts and pants to jackets and hats, bed sheets, blankets, upholstered furniture and computer mouse mats. Industrial polyester fibers, yarns and ropes are used in tyre reinforcements, fabrics for conveyor belts, safety belts, coated fabrics and plastic reinforcements with high-energy absorption. Polyester fiber is used as cushioning and insulating material in pillows, comforters and upholstery padding. Polyester fabrics are highly stain-resistant— in fact, the only class of dyes which can be used to alter the color of polyester fabric are what are known is disperse dyes.[2]

Polyester fibers are sometimes spun together with natural fibers to produce a cloth with blended properties. Cotton mixed with Polyester blends can be strong, wrinkle and tear-resistant, and reduce shrinking. Synthetic fibers in polyester also create materials with water, wind and environmental resistance compared to plant-derived fibers. Cons of cotton and polyester blends include being less breathable than cotton and trapping more moisture while sticking to the skin. They are also less fire resistant and can melt when ignited.[3]

Polyester blends have been renamed so as to suggest their similarity or even superiority to natural fibers (for example, China silk, which is a term in the textiles industry for a 100% polyester fiber woven to resemble the sheet and durability of insect-derived silk).

Polyesters are also used to make bottles, films, tarpaulin, canoes, liquid crystal displays, holograms, filters, dielectric film for capacitors, film insulation for wire and insulating tapes. Polyesters are widely used as a finish on high-quality wood products such as guitars, pianos and vehicle/yacht interiors. Thixotropic properties of spray-applicable polyesters make them ideal for use on open-grain timbers, as they can quickly fill wood grain, with a high-build film thickness per coat. Cured polyesters can be sanded and polished to a high-gloss, durable finish.

Liquid crystalline polyesters are among the first industrially used liquid crystal polymers. They are used for their mechanical properties and heat-resistance. These traits are also important in their application as an abradable seal in jet engines[citation needed].

Types

Polyesters as thermoplastics may change shape after the application of heat. While combustible at high temperatures, polyesters tend to shrink away from flames and self-extinguish upon ignition. Polyester fibers have high tenacity and E-modulus as well as low water absorption and minimal shrinkage in comparison with other industrial fibers.

Unsaturated polyesters (UPR) are thermosetting resins. They are used as casting materials, fiberglass laminating resins and non-metallic auto-body fillers. Fiberglass-reinforced unsaturated polyesters find wide application in bodies of yachts and as body parts of cars.

According to the composition of their main chain, polyesters can be:

Composition of the main chain Homo- or copolymer Examples of polyesters Examples of manufacturing methods
Aliphatic Homopolymer Polyglycolide or Polyglycolic acid (PGA) Polycondensation of glycolic acid
Polylactic acid (PLA) Ring-opening polymerization of lactide
Polycaprolactone (PCL) Ring-opening polymerization of caprolactone
Polyhydroxyalkanoate (PHA)
Polyhydroxybutyrate (PHB)
Copolymer Polyethylene adipate (PEA)
Polybutylene succinate (PBS) Polycondensation of succinic acid with 1,4-butanediol
Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) Copolymerization of 3-hydroxybutanoic acid and 3-hydroxypentanoic acid,
butyrolactone and valerolactone (oligomeric aluminoxane as a catalyst)
Semi-aromatic Copolymer Polyethylene terephthalate (PET) Polycondensation of terephthalic acid with ethylene glycol
Polybutylene terephthalate (PBT) Polycondensation of terephthalic acid with 1,4-butanediol
Polytrimethylene terephthalate (PTT) Polycondensation of terephthalic acid with 1,3-propanediol
Polyethylene naphthalate (PEN) Polycondensation of at least one naphthalene dicarboxylic acid with ethylene glycol
Aromatic Copolymer Vectran Polycondensation of 4-hydroxybenzoic acid and 6-hydroxynaphthalene-2-carboxylic acid

Increasing the aromatic parts of polyesters increases their glass transition temperature, melting temperature, thermal stability, chemical stability...

Polyesters can also be telechelic oligomers like the polycaprolactone diol (PCL) and the polyethylene adipate diol (PEA). They are then used as prepolymers.

Industry

Basics

Polyester is a synthetic polymer made of purified terephthalic acid (PTA) or its dimethyl ester dimethyl terephthalate (DMT) and monoethylene glycol (MEG). With 18% market share of all plastic materials produced, it ranges third after polyethylene (33.5%)[citation needed] and polypropylene (19.5%).

The main raw materials are described as follows:

  • Purified terephthalic acid – PTA – CAS-No.: 100-21-0
Synonym: 1,4 benzenedicarboxylic acid,
Sum formula; C6H4(COOH)2 , mol weight: 166.13
  • Dimethylterephthalate – DMT – CAS-No: 120-61-6
Synonym: 1,4 benzenedicarboxylic acid dimethyl ester
Sum formula C6H4(COOCH3)2 , mol weight: 194.19
  • Mono Ethylene Glycol – MEG – CAS No.: 107-21-1
Synonym: 1,2 ethanediol
Sum formula: C2H6O2 , mol weight: 62,07

To make a polymer of high molecular weight a catalyst is needed. The most common catalyst is antimony trioxide (or antimony tri acetate):

Antimony trioxide – ATO – CAS-No.: 1309-64-4 Molecular weight: 291.51 Sum formula: Sb2O3

In 2008, about 10,000 tonnes Sb2O3 were used to produce around 49 million tonnes polyethylene terephthalate.[citation needed]

Polyester is described as follows:

Polyethylene Terephthalate CAS-No.: 25038-59-9 Synonym/abbreviations: polyester, PET, PES Sum Formula: H-[C10H8O4]-n=60–120 OH, molelcular unit weight: 192.17

There are several reasons for the importance of Polyester:

  • The relatively easy accessible raw materials PTA or DMT and MEG
  • The very well understood and described simple chemical process of polyester synthesis
  • The low toxicity level of all raw materials and side products during polyester production and processing
  • The possibility to produce PET in a closed loop at low emissions to the environment
  • The outstanding mechanical and chemical properties of polyester
  • The recyclability
  • The wide variety of intermediate and final products made of polyester.

In table 1 the estimated world polyester production is shown. Main applications are textile polyester, bottle polyester resin, film polyester mainly for packaging and specialty polyesters for engineering plastics. According to this table, the world's total polyester production might exceed 50 million tons per annum before the year 2010.

Table 1: World polyester production

Market size per year
Product type 2002 [Million tonnes/year] 2008 [Million tonnes/year]
Textile-PET 20 39
Resin, bottle/A-PET 9 16
Film-PET 1.2 1.5
Special polyester 1 2.5
Total 31.2 59

Raw material producer

Polyester processing

After the first stage of polymer production in the melt phase, the product stream divides into two different application areas which are mainly textile applications and packaging applications. In table 2, the main applications of textile and packaging of polyester is listed.

Table 2: Textile and packaging polyester application list

Polyester-based polymer (melt or pellet)
Textile Packaging
Staple fiber (PSF) Bottles for CSD, Water, Beer, Juice, Detergents
Filaments POY, DTY, FDY A-PET Film
Technical yarn and tire cord Thermoforming
Non-woven and spunbond BO-PET Biaxial oriented Film
Mono-filament Strapping

Abbreviations: PSF = Polyester Staple Fiber; POY = Partially Oriented Yarn; DTY = Draw Textured Yarn; FDY = Fully Drawn Yarn; CSD = Carbonated Soft Drink; A-PET = Amorphous Polyester Film; BO-PET = Biaxial Oriented Polyester Film;

A comparable small market segment (much less than 1 million tonnes/year) of polyester is used to produce engineering plastics and masterbatch.

In order to produce the polyester melt with a high efficiency, high-output processing steps like staple fiber (50–300 tonnes/day per spinning line) or POY /FDY (up to 600 tonnes/day split into about 10 spinning machines) are meanwhile more and more vertically integrated direct processes. This means the polymer melt is directly converted into the textile fibers or filaments without the common step of pelletizing. We are talking about full vertical integration when polyester is produced at one site starting from crude oil or distillation products in the chain oil → benzene → PX → PTA → PET melt → fiber/filament or bottle-grade resin. Such integrated processes are meanwhile established in more or less interrupted processes at one production site. Eastman Chemicals were the first to introduce the idea of closing the chain from PX to PET resin with their so-called INTEGREX process. The capacity of such vertically integrated production sites is >1000 tonnes/day and can easily reach 2500 tonnes/day.

Besides the above-mentioned large processing units to produce staple fiber or yarns, there are ten thousands of small and very small processing plants, so that one can estimate that polyester is processed and recycled in more than 10 000 plants around the globe. This is without counting all the companies involved in the supply industry, beginning with engineering and processing machines and ending with special additives, stabilizers and colors. This is a gigantic industry complex and it is still growing by 4–8% per year, depending on the world region.

Synthesis

Synthesis of polyesters is generally achieved by a polycondensation reaction. See "condensation reactions in polymer chemistry". The general equation for the reaction of a diol with a diacid is :

(n+1) R(OH)2 + n R´(COOH)2 → HO[ROOCR´COO]nROH + 2n H2O

Azeotrope esterification

In this classical method, an alcohol and a carboxylic acid react to form a carboxylic ester. To assemble a polymer, the water formed by the reaction must be continually removed by azeotrope distillation.

Alcoholic transesterification

<templatestyles src="Module:Hatnote/styles.css"></templatestyles>

Transesterification: An alcohol-terminated oligomer and an ester-terminated oligomer condense to form an ester linkage, with loss of an alcohol. R and R' are the two oligomer chains, R'' is a sacrificial unit such as a methyl group (methanol is the byproduct of the esterification reaction).

Acylation (HCl method)

The acid begins as an acid chloride, and thus the polycondensation proceeds with emission of hydrochloric acid (HCl) instead of water. This method can be carried out in solution or as an enamel.

Silyl method
In this variant of the HCl method, the carboxylic acid chloride is converted with the trimethyl silyl ether of the alcohol component and production of trimethyl silyl chloride is obtained

Acetate method (esterification)

Silyl acetate method

Ring-opening polymerization

Aliphatic polyesters can be assembled from lactones under very mild conditions, catalyzed anionically, cationically or metallorganically. A number of catalytic methods for the copolymerization of epoxides with cyclic anhydrides have also recently been shown to provide a wide array of functionalized polyesters, both saturated and unsaturated.

Biodegradation

The futuro house was made of fibreglass-reinforced polyester plastic; polyester-polyurethane, and poly(methylmethacrylate) one of them was found to be degrading by Cyanobacteria and Archaea.[4][5]

Cross-linking

Unsaturated polyesters are thermosetting resins. They are generally copolymers prepared by polymerizing one or more diol with saturated and unsaturated dicarboxylic acids (maleic acid, fumaric acid...) or their anhydrides. The double bond of unsaturated polyesters reacts with a vinyl monomer, usually styrene, resulting in a 3-D cross-linked structure. This structure acts as a thermoset. The exothermic cross-linking reaction is initiated through a catalyst, usually an organic peroxide such as methyl ethyl ketone peroxide or benzoyl peroxide.

See also

References

  1. Lua error in package.lua at line 80: module 'strict' not found.
  2. Lua error in package.lua at line 80: module 'strict' not found.
  3. Lua error in package.lua at line 80: module 'strict' not found.
  4. Lua error in package.lua at line 80: module 'strict' not found.
  5. Lua error in package.lua at line 80: module 'strict' not found.